Product Details:
Payment & Shipping Terms:
|
Type: | Hammer Plate | Material: | High Cr Cast Iron, High Abrasion High Cr Cast Iron |
---|---|---|---|
Material Grade: | AS2074 | Size: | Customer Size |
Production Process: | Investment Cast | Surface Treatment: | Shot Blasting,Machining |
Application: | Stone,Ore,Coal Mine,Limestone | Certification: | ASTM, ISO9001:2008 |
Service: | OEM ODM |
AS2027 Cr35 High Cr Cast Iron Hammer Casting Parts for Single-Row Hammer Crushers HRC62 Hammer Head
Hammer and grates are the most important wear parts of metal shredder crusher. We use high Chromium
alloy steel as the material to make sure the quality.
Main Material: High Chromium Alloy Steel
Application:Mine, metallurgy, chemical industry, cement, petroleum etc.
Dimensions:as per drawings
Feature:
1. Suit the crusher machine rotor well
2. High toughness and impact strength
3. Good wear resistance and durable
Chemical Composition:
Standard Specification for High Chromium Cast Iron
|
||||||||||
Reference Standard
(ISO 21988-2005)
|
Nominal Chemical Composition (W%) |
Eqv. Standards
|
||||||||
C | Si | Mn | Ni | Cr | Mo | Cu | P | S | ||
ISO 21988/JN/
HBW555XCr13
|
1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 11.0-14.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 |
EN-GJN-HV600(XCr11)
ASTM A532 12% Cr
|
ISO 21988/JN/
HBW555XCr16
|
1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 14.0-18.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 |
EN-GJN-HV600(XCr14)
ASTM A532 15% Cr-Mo
AS 2027 CrMo 15 3
G-X 300 CrMoNi 15 2 1
|
ISO 21988/JN/
HBW555XCr21
|
1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 18.0-23.00 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 |
EN-GJN-HV600(XCr18)
ASTM A532 20% Cr-Mo
AS 2027 CrMo 20 1
G-X 260 CrMoNi 20 2 1
|
ISO 21988/JN/
HBW555XCr27
|
1.8-3.6 | ≤1.0 | 0.5-2.0 | ≤2.0 | 23.0-30.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 |
EN-GJN-HV600(XCr23)
ASTM A532 25% Cr-Mo
AS 2027 Cr27 LC & Cr27 HC
G-X 260 Cr27
|
ISO 21988/JN/
HBW600XCr35
|
3.0-5.5 | ≤1.0 | 1.0-3.0 | ≤1.0 | 30.0-40.0 | ≤1.5 | ≤1.2 | ≤0.06 | ≤0.06 | AS 2027 Cr35 |
ISO 21988/JN/
HBW600XCr20Mo2Cu
|
2.6-2.9 | ≤1.0 | ≤1.0 | ≤1.0 | 18.0-21.0 | 1.4-2.0 | 0.8-1.2 | ≤0.06 | ≤0.06 | AS 2027 CrMoCu 20 2 1 |