Material: | Cobalt Based Alloy | Grade: | Stellite 25 Etc |
---|---|---|---|
Size: | 3.2, 4.0, 4.8, 5.0, 6.4,7.0mm/ Customized | Specifications: | VII-106 To VII-375 |
Welding Current: | 90-120 | Operating Temperature: | 650-1100(℃) |
Hardness: | 50-55 | Type: | Machine Parts ,Wear Parts |
Feature: | Wear And Corrosion Resistance | Application: | Low Carbon Steel Structure, Thin Plate Steel, Hardfacing Welding |
Service: | OEM ODM |
Stellite 3 Seat Cobalt Chromium Tungsten Alloy Ball Seat V11-125 Cobalt Valve Seats
Product Description:
EB Stellite's cobalt base alloys are available as cobalt rods, cobalt electrodes, cobalt wire and cobalt powder. Cobalt alloys are used primarily for wear applications, our cobalt alloys can be applied by any known fusion welding process or HVOF spraying proess and are particularly well-suited for hardfacing applications. Cobalt alloys are the most widely used wear resistant hardfacing materials available. Their unique combination of wear resistance, strength and corrosion resistance make them adaptable to many harsh environments. Cobalt alloys are selected for their excellent resistance to the widest combination of wear types including adhesive wear, abrasion, erosion, contact fatigue, thermal shock, cavitation wear, corrosion and oxidation. The degree to which the cobalt alloys retain these properties assures their unique position in the wear technology field.
AWS RCoCr-C (Stellite 1)
It has excellent wear and heat resistance at high temperature.
Recommended use for making valve seal inserts , rotating sealing ring, drill heads, cutter edge ,etc
AWS RCoCr-A (Stellite 6)
The most widely used Cobalt Alloy with good mechanical properties at different temperatures,
Recommended use for making valve seat material, hot shear blade, high temperature valve , turbine blade ,etc.
AWS RCoCr-B (Stellite 12)
It has excellent resistance on high heat, corrosion and abrasion.
Recommended use for making high-pressure valve, shear edge, sawteeth, etc.
AWS RCoCr-B (Stellite 21)
It has excellent resistance on high heat, corrosion and abrasion.
Recommended use for making fuild valve,brass casting die , vlave seat, etc.
Features:
1) Powder of three main alloys: cobalt-base alloy, nickel-base alloy, and iron-base alloy, stellite alloy
2) Properties: good resistance against high-temperature, corrosion, wear, shock and stick abrasion
3) Main application: use to repair and pre-protection of valve seat, pump shaft sleeve and valve gate
4) Process: OXY, PTA, high frequency remelting
5) Specifications: 150/320, 200/400, 280/400, 180/400, 60/170, 60/200
Chemical Composition |
|||||||||
Composition (%) |
C |
Mn |
W |
S |
Si |
Cr |
Ni |
Co |
Fe |
Stellite 25 |
≤0.1 |
≤1.5 |
14.0-16.0 |
≤0.03 |
0.40-1.0 |
18.0-22.0 |
8.0-22.0 |
Bal. |
≤3.0 |